Why Glass Fiber Reinforcement?
Adding glass fiber to nylon dramatically improves mechanical properties, making it suitable for demanding applications that unreinforced nylon cannot handle.
Property Improvements
| Eigendom | PA6 | PA6 + 30% GF |
|---|---|---|
| Treksterkte | 75 MPa | 150 MPa |
| Flexural Modulus | 2,8 GPa | 7.5 GPa |
| HDT (1,8 MPa) | 70°C | 205°C |
| Vochtabsorptie | 8% | 1.5% |
Toepassingen
- Automotive: radiator end tanks, intake manifolds
- Electrical: high-temperature connectors
- Industrial: pump housings, valve bodies
Processing Guidelines
- Dry at 80-100°C for 4-6 hours
- Use wear-resistant screw
- Higher mold temperatures (60-90°C)
FAQ
How do you know whether Glass Fiber Reinforced Nylon — When Standard Isn’t Enough fits a part?
Glass Fiber Reinforced Nylon — When Standard Isn’t Enough fits a part when its load capacity, temperature range, moisture exposure, wear behavior, and processing method match the real service conditions.
What properties should be checked for Glass Fiber Reinforced Nylon — When Standard Isn’t Enough?
Controleer de sterkte, stijfheid, slagvastheid, hittebestendigheid, vochtopname, maatvastheid, wrijving, slijtage en chemische compatibiliteit.
What is the biggest selection risk for Glass Fiber Reinforced Nylon — When Standard Isn’t Enough?
Het grootste risico is dat men zich baseert op een waarde uit een datasheet zonder rekening te houden met de daadwerkelijke omgeving, de verwerkingsmethode, de geometrie van het onderdeel en het gebruik op lange termijn.
When should Glass Fiber Reinforced Nylon — When Standard Isn’t Enough be tested before production?
Het wordt aanbevolen om het onderdeel te testen wanneer het wordt blootgesteld aan belasting, hitte, chemicaliën, vocht, strenge toleranties, wettelijke voorschriften of een nieuwe bedrijfsomgeving.